Personal notes: -Depleted Uranium U-0.75Ti Alloy- Elongation: 19% Density: 18.6 g/cm3 Yield Tensile Strength: 965 MPa Ultimate Tensile Strength: 1,565 MPa -Rolled Homogeneous Armor (MIL-DTL-12560)- Elongation: 12.1% Density: 7.84 g/cm3 Yield Tensile Strength: 938 MPa Ultimate Tensile Strength: 1,111 MPa -Titanium Ti-6AL-4V (MIL-T-9046J)- Elongation: 14% Density: 4.43 g/cm3 Yield Tensile Strength: 880 MPa Ultimate Tensile Strength: 950 MPa Compressive Yield Strength: 970 MPa -Aluminum 2519-T87 (MIL-DTL-46192)- Elongation? Density: 2.823 g/cm3 Yield Strength: 400 MPa Ultimate Tensile Strength: 455 MPa -Weldalite 049-T81- Elongation: 10% Density: 2.6 g/cm3 Yield Strength: 350 MPa Ultimate Tensile Strength: 460 MPa -Magnesium AZ31B-H24- Elongation: 15% Density: 1.77 g/cm3 Yield Tensile Strength: 220 MPa Ultimate Tensile Strength: 290 MPa Compressive Yield Strength: 180 MPa